After inquiring into physical characteristics of using fly ash and alkali solution, it was found that higher pH density is favorable to strength development at early age and the higher the age is, the higher the compressive strength gets. Also, it was found that when there is more addition of activator, the compressive strength is higher. I was shown that more than atmospheric curing, steam curing was favorable for development of compressive strength. When the temperature of curing temperature was higher, most of the compressive strengths were higher. Thus, based on this study, it was understood that environmental-friendly chemically combined concrete using fly ash and alkali solution can be utilized without using cement. |